Double metal composite material:
Ti/Cu,Zr/Cu,Ni/Cu,Tan/Cu, Stainless steel/Cu ,Ti/Al
conductivity and corrosion resistance
Titanium clad Copper busbar
Ti:Gr2
Cu:C11000
Size:82.4mm(wideth)*20mm(thickness)*3160mm*drawing (Ti thickness:1.5mm)
Titanium clad Copper busbar
Ti(Gr2) Cu(C11000)
Ti:ASTMB338 Cu:ASTMB187
66mm*24mm*3000mm (Ti thickness:2.0mm)
Titanium clad Copper busbar
Ti:Gr2
Cu:C11000
Size:27mm(wideth)*12mm(thickness)*drawing (Ti thickness:1.0mm)
Titanium Copper clad bending punching formed parts
Ti:Gr2 Cu:C11000
GB/T12769-2003
102*22*1584*drawing (Ti thickness:1.0mm)
Titanium Copper clad bending punching formed parts
Ti:Gr2 Cu:C11000
GB/T12769-2003
102*22*1584*drawing (Ti thickness:1.0mm)
Ti:Gr2 ASTM B338 Cu:C11000 ASTM B187
GB/T12769-2003
Size:120mm(width)*19mm(thickness)*380mm*drawing (Ti thickness:2.0mm)
Titanium Copper clad bending punching formed parts
Ti:Gr2 Cu:C11000
GB/T12769-2003
102*22*1584*drawing (Ti thickness:1.0mm)
Ti:Gr2 ASTM B338 Cu:C11000 ASTM B187
GB/T12769-2003
Size:120mm(width)*19mm(thickness)*380mm*drawing (Ti thickness:2.0mm)
Zirconium clad Copper busbar mainly used in strong corrosive conditions of a conductor as a electrode.
Stainless steel clad Copper with high conductivity, strong corrosion resistance,cheaper than Titanium clad Copper.
Titanium Copper clad bending punching formed parts
Ti:Gr2 Cu:C11000
GB/T12769-2003
50.4*14.4*1862.5mm (Ti thickness:1.0mm)
Titanium copper clad welding punching formed parts
Ti:Gr2 Cu:C11000
102*18*1764mm (Ti thickness:1.5mm)
Ti:Gr2 ASTM B338 Cu:C11000 ASTM B187
GB/T12769-2003
Size:50mm(wideth)*11mm(thickness)*1890mm*drawing (Ti thickness:1.0mm)
Titanium clad Copper busbar
Ti:Gr2
Cu:C11000
Size:82.4mm(wideth)*20.4mm(thickness)*1570.5mm*drawing (Ti thickness:1.5mm)
On the premise of guarantee the conductive be used to support the role of copper in commen steel replacement,reduces the cost
Titanium Copper clad bending punching formed parts
Ti:Gr2 Cu:C11000
GB/T12769-2003
40*10*drawing (Ti thickness:1.0mm)
Stainless steel clad Copper with high conductivity,corrosion resistance,cheaper than Titanium clad Copper as the electrode.